What Is Bend?
The bend test is a test in which the specimen is bent around a defined mandrel, or at a defined support span, to a specified angle, evaluating whether cracks form on the outer surface.
Purpose of Bend
The purpose is to verify the ductility and cold-forming capability of the material or welded joint against the acceptance criterion.
Which Products Is Bend Applied To?
- Sheet and strip products
- Pipe and section
- Welded joints
- Construction reinforcing steel
In Which Sectors Is Bend Used?
Standards Related to Bend
- ISO 7438
- ASTM E290
- ISO 5173 (welding)
- ISO 15630 (reinforcement)
Bend Conditions
- Bend angle
- Defined in the product standard (e.g. 90°, 180°)
- Mandrel diameter
- A multiple of thickness defined in the standard
- Bending method
- Mandrel, V-block or guided bending
- Temperature
- Room temperature, unless otherwise stated
Equipment for Bend
- Bend test rig and press
- Standard mandrel set
- Angle-measurement rig
- Magnifier or stereo microscope
Sample Requirements for Bend
- Specimen width and thickness must conform to the standard
- Edges must be notch-free; rounded if required
- The weld location must be defined for a welded specimen
- The number of specimens is defined in the product standard
Duration of Bend
Typically 1–2 days, including specimen preparation.
Bend Procedure
- 1The specimen is prepared per the standard.
- 2The mandrel diameter and bend angle are determined.
- 3The specimen is bent to the defined angle.
- 4The outer surface is examined for cracks.
- 5Findings are compared with the acceptance criterion.
Bend Acceptance Criteria
The acceptance criterion is given in the product standard; generally the absence of a crack exceeding a defined size on the outer surface is required.
Evaluation of Results
Edge cracks may be a preparation defect rather than a material defect; most standards evaluate edge cracks separately.
Bend Report
- Standard applied
- Specimen dimensions and direction
- Mandrel diameter and bend angle
- Visual-inspection findings
- Assessment
Accreditation
EUROLAB holds internationally recognised accreditation obtained from accreditation bodies party to the IAF and ILAC multilateral recognition arrangements, under ISO/IEC 17025 for laboratory testing, ISO/IEC 17020 for inspection and surveillance, and ISO/IEC 17021-1 and ISO/IEC 17065 for system and product certification. This chain ensures the reports and certificates issued are accepted worldwide.
Whether this test can be offered within accredited scope depends on your product and the standard applied; since accreditation is method-based, the scope is confirmed in writing at the quotation stage.
Scope and authorisationsRelated Regulations
- Product standards
- Welding-procedure specifications
Metal and Metallurgy Testing — What Does This Testing Field Cover?
The section below describes the field that the Bend test belongs to; the conditions and acceptance criteria of this particular test are given in the sections above. The scope specific to your product is confirmed in writing at the quotation stage.
Metal and metallurgical testing determines the load a metal or a welded joint can carry, how it fails and what its internal structure looks like. The output of this family is often not about the product itself but about the identity of the MATERIAL: is the steel really of the declared grade, does the weld seam deliver the strength the design assumes, does the casting contain an unacceptable internal defect?
The practical importance of the field comes from the fact that a metal part rarely fails gradually. A plastic part deforms, ages, cracks and usually gives warning. A weld seam or a fastener, by contrast, often breaks without warning — especially where fatigue and brittle fracture are involved. That is why in fields such as pressure equipment, lifting gear, structural steel and pipelines, material testing is a requirement of REGULATION rather than of design.
The family brings together three groups of methods, and each answers a different question. Mechanical tests quantify how the material behaves under load. Non-destructive examination looks for defects without damaging the part. Metallography and chemical analysis explain why the material behaves the way it does — through grain structure, phase distribution, inclusion content and alloy composition.
The acceptance criterion for these tests almost never comes from the test standard, and this is the key to understanding the field. The test standard says how the measurement is to be made; the acceptable values come from the product standard, the material grade or the fabrication code. ISO 6892-1 tells you how to run a tensile test; EN 10025 tells you what yield strength that steel must deliver. When reading a report, the product standard it was assessed against is essential.
Sampling is an inseparable part of the result in this field. Two specimens taken from the same heat may give different values depending on the direction and location they were taken from; in rolled products, specimens parallel and perpendicular to the rolling direction produce different results. Product standards therefore also govern sampling location and orientation, and the report must document this.
Method groups in this field
Mechanical tests
Tensile, compression, bending, notch impact (Charpy), hardness (Brinell, Vickers, Rockwell), fatigue, creep and fracture toughness. These give the behaviour of the material under load in numerical form.
Non-destructive examination
Radiography, ultrasonic examination, penetrant, magnetic particle and visual examination. It looks for surface and internal defects without damaging the part and is an indispensable step in welded fabrication.
Metallography
Specimen preparation, etching and microscopic examination. Grain size, phase distribution, inclusion content, case depth and the weld heat-affected zone are assessed.
Chemical analysis
Alloy composition is verified by optical emission spectrometry and wet chemistry; confirmation of the material grade runs through this step.
Corrosion behaviour
Salt spray, pitting and crevice corrosion and intergranular corrosion tests. In stainless steels these can indicate the quality of the heat treatment.
Commonly confused in this field
- A material certificate (such as EN 10204 3.1) is not a test report; it is the manufacturer's declaration. In critical applications independent verification is carried out, and the two must not be confused.
- ASTM and ISO tensile tests measure the same quantities but use different specimen geometries; the results are not treated as directly equivalent, and whichever the specification calls for is the one applied.
- Conversion tables between hardness and strength are APPROXIMATE. Calculating yield strength from hardness is not sufficient evidence for material acceptance.
- In non-destructive examination, "no defect found" does not mean there is no defect; defects below the detection limit of the method may be present. The report must state the method applied and the sensitivity level.
- A weld seam passing does not show that the welder or the procedure is qualified; these are separate processes.
Which decisions these results support
- Verifying the material certificate and accepting incoming material
- Approving welded fabrication; welder and procedure qualification
- Manufacturing control of pressure equipment and structural components
- Failure analysis and determining the root cause of field damage
- Verifying heat treatment and surface treatment processes
Related Tests
Frequently Asked Questions About Bend
According to which standard is Bend made?
Bend is executed in scope ISO 7438, ASTM E290, ISO 5173 (welding) and ISO 15630 (reinforcement). The limit values and acceptance criteria to be applied are defined in the product standard; The version valid for your product is confirmed in writing at the offer stage.
Which products does Bend apply to?
Mainly applied to Sheet and strip products, Pipe and section, Welded joints and Construction reinforcing steel. Whether your product is included in the scope is determined by examining its technical specifications and intended use.
Under what conditions is Bend done?
The determining parameters are: Bend angle — Defined in the product standard (e.g. 90°, 180°), Mandrel diameter — A multiple of thickness defined in the standard and Bending method — Mandrel, V-block or guided bending. The full terms are in the "Test Conditions" section on the page and vary depending on the product standard.
What kind of sample is needed for Bend?
Specimen width and thickness must conform to the standard, Edges must be notch-free; rounded if required and The weld location must be defined for a welded specimen. The number of samples is determined according to the product standard and the scope to be reported.
How long does Bend take?
Typically 1–2 days, including specimen preparation. This duration belongs to the experiment itself; sample preparation, queuing and reporting are also evaluated. A realistic schedule for your product is given in the offer.
What is the Bend result called "appropriate"?
The acceptance criterion is given in the product standard; generally the absence of a crack exceeding a defined size on the outer surface is required.